产品描述 Product Describe | 25%玻璃纤维增强聚酰胺6 25%Glass Fiber Reinforced PA6 | ||
产品等级 Grade | 增强级 Reinforced | ||
外观 Appearance | 粒状,本色 Pellet, Nature Color | ||
产品性能参数 Data Sheet | |||
项目 Item | 典型性能 Typical Characteristic | 测试标准 Testing Standard | |
机械性能Mechanical Properties | |||
| 拉伸强度Tensile Strength | 159 MPa | ISO527, 50mm/min | |
| 断裂伸长率Elongation at break | 3.3% | ISO527, 50mm/min | |
| 弯曲强度Flexural Strength | 216 MPa | ISO178, 2mm/min | |
| 弯曲模量Flexural Modulus | 6416 MPa | ISO178, 2mm/min | |
简支梁缺口冲击强度 Charpy Impact notched | 13.2 KJ/m2 | ISO179 | |
简支梁无缺口冲击强度 Charpy Impact unnotched | 90.6 KJ/m2 | ISO179 | |
| 洛氏硬度Rockwell Hardness | 117 | ISO2039/2 | |
热性能Thermal Properties | |||
热变形温度 Heat Distortion Temp. | 0.45MPa | ISO75 | |
| 1.81MPa | 201 ℃ | ISO75 | |
| 熔点Melting Point | 220 ℃ | ISO3146C | |
电性能Electrical Properties | |||
| 体积电阻率Volume Resistant | IEC93 | ||
| 表面电阻率Surface Resistant | 1012 Ω | IEC93 | |
| 介电强度Dielectric Strength | IEC 60243-3 | ||
| 电痕化指数Comp Track Index | IEC 60112 | ||
其它Others | |||
| 密度Specific Gravity | 1.31 g/cm3 | ISO1183 | |
| 灰分Ash Content | 25±2 | ISO3451-4 | |
| 吸水率Water Absorption | ≈2.0 | ISO62 | |
| 模塑收缩率Mold Shrinkage | 0.2 / 0.5 | ISO294-4 | |
| 燃烧性能 | |||
| UL垂直燃烧Flammability | HB | UL-94 | |
灼热丝可燃指数 Glow-wire Flammability Index | IEC 60695-2-12 | ||
PA6干燥处理
干燥处理：由于PA6很容易吸收水分，因此加工前的干燥特别要注意，如果材料是用防水材料包装供应的，则容器应保持密闭。如果湿度大于0.2%，建议在80℃以上的热空气中干燥16小时。如果材料已经在空气中暴 露超过8小时，建议进行温度为105℃，8小时以上的真空烘干。融化温度：230-280℃，对于增强品种为250-280℃。模具温度：80-90℃。模具温度很***地影响结晶度，而结晶度又影响着塑件的机械特性。
PA6玻纤增强材料可根据产品的特性要求添加玻纤含量在5-60%的范围，这类材料具有很好的强度、耐热性能、优良的抗冲击性能、良好的尺寸稳定性及低翘曲性等。